dedicated polymer Elastomers Inquiry
 

Nonwovens Fabrics & Chemical Fiber dedicated polymer Elastomers


We use metallocene catalysis system to produce propenyl Elastomer. The synthesis of the polymer is of high stereotacticity. And it has narrow relative molecular weight. From that we can accuratelycontrol the physical and mechanical properties, also the processing properties of Polymers.  The products owns very high elasity, meanwhile it also has high flowability.  Our products can totally replace the usage of the Cooling Masterbatch.  Our products provides modification for multi-field polyolefin system.

Index of Physical Property

Appearance:Transparent, granulated

Melt Index :18~6000g/10min

Density:0.87g/cm3

Shore Hardness:35~84A

Softening Point:65~105℃

Melting Point:65~105℃

Nonwovens Test Data

常數

Item

無紡布克重為9g3.2米線。測試溫度;25℃,濕度35%。強度測試拉伸速度:500mm/min,試樣寬度:100mm,夾距:75mm,無預加張力。

9 grams of Nonwovens Fabrics, 3.2 meters Line, 25℃ testing temperatue, 35% of humidity,   500mm/min tensile speed of tensile strength testing,  100mm of specimen width,  75mm of clip distance, and with no pre-tension

添加比例

Adding  Percentage/ Proportion

斷裂強度(N)

Breaking Tenacity

提升幅度(%)

Lifting Range

橫向

Horizontal

純原料+3.0%降溫母粒+26%填充料

Pure raw materials+3.0%Cooling Masterbatch+26% Filler Masterbatch

7.20

9

 

純原料+26%填充料+3.0%專用彈性體

Raw materials+26%Filler Masterbatch+3.0% Dedicated Elastomers

8.20

縱向

Vertical

純原料+3.0%降溫母粒+26%填充料

Pure raw materials+3.0%Cooling Masterbatch+26% Filler Masterbatch

10.00

15

純原料+26%填充料+3.0%專用彈性體

Raw materials+26%Filler Masterbatch+3.0% Dedicated Elastomers

11.6

 

Adding this product can increase theTensile Strength of Nonwovens Fabrics.  it can totally replace the function of Cooling Masterbatch. And at the same time, it can improve the softness, handfeeling of  Nonwoven s Fabrics. Adding the products  can also extend the aging time of the Nonwovens, from thus customers can reduce the cost of production.

 

 

 

 




Clicks:84904  Date:2017/8/22 【Print】 【Back  
  Copyright © 2014 www.mlnlay.live All rights reserved
Tel:+86-571-85095115 Email:[email protected] |
Address:Canghexia No. 36, Tiyuchang Road, Xiacheng District, Hangzhou, Zhejiang, China
网球频道